Fortunately, there are several parts of design such as hinges, fiber optic connector bases, and new style connectors are closely dependent on MIM technology. These products are being produced in a large number and MIM technology is being adopted by more and more.
MIM and CIM--Drome can provide one-stop service solution.
The basic attributes include:
1.Economical production of complex parts with weight from 0.03 to 200g from high-performance engineering materials.
2.Parts with high dimensional precision (±0.1%~±0.5%) and good surface quality (surface roughness 1~2μm).
3.Parts with high relative density (96%~100%), homogeneous microstructure and superior performance.
4.Adaptable to powders of various materials and wide application of the parts.
5.Material saving through the recycle of wastes, production process with high level of automation and suitable for mass production
Flow chart of metal injection molding
Application of MIM
Products Range:
Â
| Material | Â | Typical Values | Â | Â | ||||
| Designation Code | Density g/cm3 | Tensile Properties | Young's modulus, Gpa | Un-notched Charpy Impact Energy,J | Hardness,Rockwell | |||
| Â | Â | UTS. Mpa | Y.S. (0.2%), Mpa | Elongation (in 25.4mm) % | Â | Â | Macro (apparent) | Â Micro (converted) |
| MIM-Fe2Ni | 7.8 | 280 | 115 | 25 | Â | Â | 55 HRB | 50HRCÂ Â Â Â |
| MIM-Fe8Ni | 7.8 | 450 | Â | 12 | Â | Â | 84HRB | 50HRCÂ Â Â Â |
| MIM-2200 (as sintered) | 7.8 | 290 | 125 | 40.0 | 190 | 135 | 45 HRB | Â |
| MIM-2700 (as sintered) | 7.8 | 415 | 255 | 26.0 | 190 | 175 | 69 HRB | Â |
| MIM-4605 (as sintered) | 7.8 | 440 | 205 | 15.0 | 200 | 70 | 62 HRB | Â |
| MIM-4605 (Q&T) | 7.8 | 1655 | 1480 | 2.0 | 205 | 55 | 48 HRC | 55 HRC |
| MIM-304L | 7.8 | 500 | Â | 70 | Â | Â | 60 HRB | Â |
| MIM-316L (as sintered) | 7.85 | 520 | 175 | 50.0 | 190 | 190 | 67 HRB | Â |
| MIM-410 | 7.7 | 900 | Â | 7 | Â | Â | Â | 40 HRC |
| MIM-420 (heat treated) | 7.7 | 1380 | 1200 | 12 | 190 | 40 | Â | 45-60HRC |
| MIM-430L (as sintered) | 7.8 | 410 | 240 | 25.0 | 210 | 150 | 65 HRB | Â |
| MIM-440C | 7.8 | 700 | 590 | 15 | Â | Â | Â | 45-60HRC |
| MIM-17-4PH (as sintered) | 7.8 | 900 | 730 | 6.0 | 190 | 140 | 27 HRC | Â |
| MIM-17-4PH (heat treated) | 7.8 | 1190 | 1090 | 6.0 | 190 | 140 | The STL water-jacketed Gold Concentrator is a kind of gravity separation equipment. It was developed by Changchun Gold Research Institute Co., Ltd. in 1985 and entered the market. At present, it has been used in many domestic and foreign companies. It is suitable for the recovery of single gold in placer gold, vein gold mines and polymetallic mines, instead of mercury plate operations. The addition of large single gold particles in the collected ore before flotation can further increase the recovery rate of gold mines, and it can also be used from gold-bearing mines. Separate single gold from flotation gold-copper concentrate and flotation gold concentrate. The main indicators of this series of equipment basically reach the level of similar international products (such as Nielsen gold selectors, etc.). Compared with similar equipment at home and abroad, this series of equipment has the advantages of high cost performance, easy operation, and low maintenance costs. Mini Gold Concentrator,Gold Extraction Machines,Commercial Gold Mining Equipment,Professional Gold Mining Equipment Changchun Gold Research Institute Co.LTD , https://www.changchungoldresearch.com | |